HIGH TEMP. SEALING CEMENT
Next »



• Physical Properties
» Coefficient of thermal expansion, In / In / oF
4.6 x 10-6
» Color
Off White
» Compressive strength, PSI
3900
» Density, Lbs / ft3
141
» Dielectric Constant
5.0 - 7.0
» Dielectric Strength at 70oF, volts / mil
25.0 - 51.0
» Dielectric Strength at 750oF, volts / mil
12.5 - 25.0
» Dielectric Strength at 1475oF, volts / mil
£1.3
» Maximum Service Temperature,of (oC)
1550 (843)
» Tensile Strength, PSI
425
» Thermal Conductivity, Btu-in/ft2 hr-of
8
» Volume Resistivity At 70oF,W-cm
107 - 109
» Volume Resistivity At 750oF, W-cm
104 - 106
» Volume Resistivity At 1475oF, W-cm
102 - 103
» Absorption, %
10 - 12
» Shrinkage, %
0.5
» Mix Ratio
Mix 3 parts powder to 1 part liquid by weight.
» Curing Schedule
CC High Temperature Cement hardens with an integral chemical-setting action with an initial set in approximately 30 minutes. The final set is reached in 18 to 24 hours when cured at room temperature. If it is desired to accelerate the curing time, set the drying oven to 150oF and the cement will cure in 4 hours. If the drying oven is set to 220oF, the cement will cure in 3 hours.
» Distinguishing Characteristics and Applications
Used to cement on and insulates Thermocouples for surface Temperature Measurement / Heater etc.


Heavy Duty Multipol Connectors

Heavy Duty Multipol Connectors


Color Codes For Thermocouple Extension & Compensating Cable

Color Codes For Thermocouple Extension & Compensating Cable

Heavy Duty Multipol Connectors
Color Codes For Thermocouple Extension & Compensating Cable
Thermocouple Codes / Conductor Combinations

Thermocouple Codes / Conductor Combinations

HAMI-THERM Standard Connectors

HAMI-THERM Standard Connectors

Thermocouple Codes / Conductor Combinations
HAMI-THERM Standard Connectors